Evaluation of reactive Si and Al amounts in various geopolymer precursors by a simple method
authors Buruberri, LH; Tobaldi, DM; Caetano, A; Seabra, MP; Labrincha, JA
nationality International
journal JOURNAL OF BUILDING ENGINEERING
author keywords Biomass fly ash; Spectrophotometric techniques; Precursor's reactivity; Geopolimerization
keywords FLY-ASH; TRACE-ELEMENTS; SPECTROPHOTOMETRIC METHOD; ALKALI ACTIVATION; DISSOLUTION; MECHANISM; BEHAVIOR; COAL; METAKAOLIN; EVOLUTION
abstract The soluble amount of Si and Al in biomass fly ash (BFA) and metakaolin (MK) was determined by using a spectrophotometric (colorimetric) method. This low-cost technique is simple to operate, and shows high selectivity and suitable sensitivity. Molybdenum blue and eriochrome cyanine R (ECR) methods were used to quantify, respectively, the SiO2 and Al2O3 amounts leached out to a sodium hydroxide solution (10 mol dm(-3)). The obtained results were compared with the chemical composition of the precursors and their amorphous phase amounts. The soluble amount of SiO2 was 7.5 wt% for BFA, and 40.3 wt% for MK. Values equal to 6.3 wt% for BFA and 35.2 wt% for MK were estimated for Al2O3. These results are quite comparable with those obtained through the combination of X-ray fluorescence (XRF) and X-ray diffraction (XRD) using fully quantitative phase analysis (FQPA): soluble SiO2 equal to 4.4 wt% for BFA and 46.1 wt% for MK, and soluble Al2O3 equal to 10.0 wt% for BFA and 35.5 wt% for MK. Then, BFA- and MK-based geopolymers were formulated, taking into account the soluble Si and Al contents estimated by the colorimetric methods, testing three distinct (2.5, 3.3 and 4.5) SiO2/Al2O3 molar ratios (R-S/A) and curing times (15, 21 and 28 days). The BFA reaction degree (alpha) and the compressive strength of the obtained samples were determined to validate the reliability of the spectrophotometric estimations. A linear correlation between the two variables was observed in BFA-based geopolymers for curing times >= 21 days. At the same time, MK and BFA based samples formulated with a fixed R-S/A, adjusted by adding silica fume, show similar compressive strength values. The use of this spectrometric technique to evaluate the amount of reactive components (Si and Al) in the precursors is an interesting tool for the design of, and to predict the performance of, the cured material.
publisher ELSEVIER SCIENCE BV
issn 2352-7102
year published 2019
volume 22
beginning page 48
ending page 55
digital object identifier (doi) 10.1016/j.jobe.2018.11.017
web of science category Construction & Building Technology; Engineering, Civil
subject category Construction & Building Technology; Engineering
unique article identifier WOS:000457639900005

Sponsors

1suponsers_list_ciceco.jpg