The Influence of PSA Pre-Anodization of AA2024 on PEO Coating Formation: Composition, Microstructure, Corrosion, and Wear Behaviors
authors Serdechnova, M; Karpushenkov, SA; Karpushenkava, LS; Starykevich, M; Ferreira, MGS; Hack, T; Iuzviuk, MH; Zobkalo, IA; Blawert, C; Zheludkevich, ML
nationality International
journal MATERIALS
author keywords AA2024; plasma electrolytic oxidation; phosphoric-sulfuric acid anodizing; corrosion resistance; wear resistance; post-treatment
keywords PLASMA ELECTROLYTIC OXIDATION; ALUMINUM-ALLOYS; CERAMIC COATINGS; CHROMATE
abstract In the frame of the current work, it was shown that plasma electrolytic oxidation (PEO) treatment can be applied on top of phosphoric sulfuric acid (PSA) anodized aluminum alloy AA2024. Being hard and well-adherent to the substrate, PEO layers improve both corrosion and wear resistance of the material. To facilitate PEO formation and achieve a dense layer, the systematic analysis of PEO layer formation on the preliminary PSA anodized layer was performed in this work. The microstructure, morphology, and composition of formed PEO coatings were investigated using scanning electron microscopy (SEM), x-ray diffraction (XRD), and glow-discharge optical emission spectroscopy (GDOES). It was shown that under constant current treatment conditions, the PSA layer survived under the applied voltage of 350 V, whilst 400 V was an intermediate stage; and under 450 V, the PSA layer was fully converted after 5 min of the treatment. The comparison test with PEO formation on the bare material was performed. It was confirmed that during the "sparking" mode (400 V) of PEO formation, the PEO coatings, formed on PSA treated AA2024, were more wear resistant than the same PEO coatings on bare AA2024.
publisher MDPI
issn 1996-1944
year published 2018
volume 11
issue 12
digital object identifier (doi) 10.3390/ma11122428
web of science category Materials Science, Multidisciplinary
subject category Materials Science
unique article identifier WOS:000456419200086
  ciceco authors
  impact metrics
journal analysis (jcr 2017):
journal impact factor 2.467
5 year journal impact factor 3.325
category normalized journal impact factor percentile 61.228
dimensions (citation analysis):
altmetrics (social interaction):



 


Sponsors

1suponsers_list_ciceco.jpg