Dielectric, Piezoelectric Enhancement and Photoluminescent Behavior in Low Temperature Sintered Pr-Modified Ba0.85Ca0.15Zr0.1Ti0.9O3 Ceramics
authors Ramovatar; Coondoo, I; Satapathy, S; Kumar, N; Panwar, N
nationality International
journal JOURNAL OF ELECTRONIC MATERIALS
author keywords Lead-free piezoelectrics; dielectric properties; photoluminescence properties
keywords LUMINESCENCE; TRANSITIONS
abstract Pristine and 0.04 wt.% Pr6O11 substituted Ba0.85Ca0.15Zr0.1Ti0.9O3 (BCZT) lead-free ceramics have been synthesized by the conventional solid-state reaction method at 1450 and 1300 degrees C sintering temperatures, respectively. The synthesized compounds were characterized by their structural, microstructural, piezoelectric, dielectric and luminescent properties. Coexistence of tetragonal and orthorhombic phases was observed for both pure and Pr doped BCZT compounds. Higher piezoelectric coefficient (d(33)) similar to 220 pC/N, maximum dielectric constant (epsilon(m)) similar to 4204 and minimum dielectric loss (tan delta) similar to 0.025 were obtained for Pr doped compound as compared to 180 pC/N, 3353 and 0.034 values, respectively, for the undoped BCZT ceramics. Strong photoluminescence emission spectra consisting of blue (489 nm), green (530 nm) and red (602 nm) light emissions were observed in Pr doped compound. Our results demonstrate that Pr6O11 addition in BCZT ceramics is helpful in increasing the electrical properties, inducing the luminescent effect and simultaneously reducing the sintering temperatures of BCZT. The results have been understood in the light of Pr3+ ions occupying the Ti4+-sites.
publisher SPRINGER
issn 0361-5235
year published 2018
volume 47
issue 10
beginning page 5870
ending page 5878
digital object identifier (doi) 10.1007/s11664-018-6472-6
web of science category Engineering, Electrical & Electronic; Materials Science, Multidisciplinary; Physics, Applied
subject category Engineering; Materials Science; Physics
unique article identifier WOS:000443021000030
  ciceco authors
  impact metrics
journal analysis (jcr 2017):
journal impact factor 1.566
5 year journal impact factor 1.614
category normalized journal impact factor percentile 39.160
dimensions (citation analysis):
altmetrics (social interaction):



 


Apoio

1suponsers_list_ciceco.jpg