Dielectric barrier formation and tunneling magnetoresistance effect in strontium iron molybdate


A comparative X-ray diffraction study of the initial single-phase metal-oxide compound-strontium iron molybdate Sr2FeMoO6 - delta (SFMO)-and that subjected to additional isothermal annealing shows that this heat treatment leads to the appearance of a SrMoO4 (SMO) phase. Small-angle neutron scattering measurements indicate that the SMO phase forms a dielectric shell surrounding SFMO grains, which has a characteristic thickness of 2-4 nm and extends above 120 nm. The character of the temperature dependence of the electric resistance corresponds to the metal-type conduction in single-phase SFMO and changes to a semiconductor type in the material with SMO dielectric shells, which is evidence of a tunneling mechanism of charge transfer. This conclusion is confirmed by an increase in the absolute value of the negative magnetoresistance of SFMO due to the appearance of a tunneling magnetoresistance component of the same sign.




Dem'yanov, SE; Kalanda, NA; Kovalev, LV; Avdeev, MV; Zheludkevich, ML; Garamus, VM; Willumeit, R

nossos autores


Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".