Synthesis of High Surface Area Carbon Nanospheres with Wrinkled Cages and Their CO2 Capture Studies

resumo

In this work, we report the synthesis protocol for carbon coated dendritic fibrous nanosilica (DFNS@Carbon) and high surface area wrinkled carbon nanospheres using phenol formaldehyde polymerization chemistry. We have shown that the choice of hard template, i.e. DFNS with different sizes and fiber density, can lead to the synthesis of carbon-coated DFNS and wrinkled carbon nanospheres with tunable properties, having high surface area (1090 +/- 50m(2)/g), large pore volume (1.18 +/- 0.02cm(3)/g) and distinct pore size distribution (from 3.5nm to 15nm). The CO2 capture value of 1.47mmol/g was obtained without any amine functionalization. This value is comparable or better than reported non-amine functionalized CO2 sorbents, indicating the contribution of textural properties and morphology of carbon cages on their CO2 capture capacity.

palavras-chave

CAPACITIVE ENERGY-STORAGE; FIBROUS NANOSILICA; SPHERES; SIZE; SUPERCAPACITOR; NANOPARTICLES; GRAPHENE; KCC-1; PERFORMANCE; CONVERSION

categoria

Chemistry

autores

Singh, B; Maity, A; Polshettiwar, V

nossos autores

Grupos

agradecimentos

We thank the Department of Atomic Energy (DAE), Government of India, and DST-CEFIPRA for funding. We sincerely acknowledge TIFR electron microscopy and Raman spectroscopy facilities.

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".