Oxygen vacancies as a link between the grain growth and grain boundary conductivity anomalies in titanium-rich strontium titanate


Titanium-rich (Sr/Ti = 0.995) strontium titanate (ST) ceramics, air-sintered in a temperature range of 1400-1625 degrees C, were reported to possess anomalies in the grain growth and analogous anomalies in the grain boundary (GB) conductivity activation energy. However, these two interface-related phenomena, occurring at GBs, could not be associated with each other using a simple "brick-layer" model. In this work we revise the topic and advocate that the deviation from the model comes from the oxygen vacancies localized at GBs of the rapidly cooled ST ceramics. To verify this, we annealed the ceramics in oxygen and performed their systematic and comparative analysis using impedance spectroscopy. A levelling-off in the GB conductivity activation energy, which increases for <= 1.24 eV, and a four-fold decrease in the GB permittivity are observed after annealing. Thus, we confirm a key role of oxygen vacancies in relation between the grain growth and GB conductivity anomalies of as-sintered Ti-rich ST ceramics.




Materials Science


Tkach, A; Amaral, L; Vilarinho, PM; Senos, AMR

nossos autores


This work was developed within the scope of the project CICECO-Aveiro Institute of Materials, POCI-01-0145-FEDER-007679 (FCT Ref. UID /CTM /50011/2013), financed by national funds through the FCT/MEC and when appropriate co-financed by FEDER under the PT2020 Partnership Agreement as well as within FCT independent researcher grant IF/00602/2013. L.A. acknowledges FCT for postdoctoral research grant SFRH/BPD/97453/2013. Thanks to Dr RC Pullar for assisting with the English language of this article.

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".