Effect of cellulose structure on reactivity of eucalyptus acid sulphite dissolving pulp
authors Ferreira, JC; Evtuguin, DV; Prates, A
nationality International
author keywords Sulphite pulping; Dissolving pulp; Chinese filterability; Fock reactivity; Eucalyptus globulus
abstract Three industrial Eucalyptus globulus acid sulphite dissolving pulps of different intrinsic viscosity (ca. 490-570 cm(3)/g) with similar xylan content (2.4-3.0%) were partially (ca. 60%) converted to cellulose II by treatment with 12% NaOH and hornified by drying for 8 h at 105 degrees C to induce changes in physical structure. All three initial and modified pulps were analysed on their Fock reactivity method and Chinese filterability. These dissolving pulps were also examined for the crystallinity degree and the crystallite dimensions assessed by wide-angle X-ray scattering and the fibril aggregation assessed by solid-state C-13 nuclear magnetic resonance. The results showed that the reactivity of the dissolving pulp was negatively correlated with the degree of cellulose crystallinity and depended almost linearly on the lateral dimension of the fibril and the dimensions of the fibril aggregates. In hornified pulps, the effect of cellulose physical structure on reactivity was even more pronounced than the intrinsic viscosity of the dissolving pulp. In addition, no unambiguous dependence between the reactivity and the filterability of dissolving pulps was found. Filterability did not correlate clearly with lateral dimension of fibril or fibril aggregates, but depended only on pulp viscosity.
publisher SPRINGER
issn 0969-0239
isbn 1572-882X
year published 2020
volume 27
issue 8
beginning page 4763
ending page 4772
digital object identifier (doi) 10.1007/s10570-020-03092-y
web of science category Materials Science, Paper & Wood; Materials Science, Textiles; Polymer Science
subject category Materials Science; Polymer Science
unique article identifier WOS:000521014700001
  ciceco authors
  impact metrics
journal analysis (jcr 2019):
journal impact factor 4.21
5 year journal impact factor 4.512
category normalized journal impact factor percentile 92.816
dimensions (citation analysis):
altmetrics (social interaction):