One-pot synthesis of poly-(3-hexylthiophene) with variable degrees of molar mass and regioregularity

resumo

Polyalkylthiophenes are applied in the form of thin films as active layers in organic devices. The main properties defined in the synthetic procedure that can affect the film formation are the molar mass and regioregularity degree (the content ofhead-to-tail, HT, linkages). These properties can be varied, at principle, by changing the conditions of the oxidative polymerization process. In this work, we evaluate the effect of oxidant addition rate, temperature and time dependence of poly-(3-hexylthiophene), P3HT, oxidative polymerization in molar mass and regioregularity degree, besides other polymer properties such as absorption and emis- sion ofvisible light. The results show that the polymer started to grow during the oxidant addition and already presents a relatively high molar mass (ca. 10,000 g/mol) just after the addition stopped. Polymerization temperature is more signif- icant in molar mass variations than the time expended for the polymerization reaction, with values of Mw ranging from 15,000 to 70,000 g/mol in the conditions tested. The HT contents were all above 70%, with higher variations in the two first hours of polymerization reaction and are mainly defined during the oxidant addition, which leads to higher HTcontents and narrower molar mass distributions using slower additions. The solvent extraction reveals that the HT content is directly

autores

Facchinatto, W. M.; Torres, B. B. M.; Balogh, D. T.

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".