Dielectric relaxation of shallow donor in polycrystalline Mn-doped ZnO

resumo

The dielectric properties of Mn-doped ZnO ceramics with electrically active grain boundaries at low temperatures of 10-70 K were investigated by admittance spectroscopy. It was observed that the dielectric relaxation of the main shallow donors, zinc interstitial, in these samples occurred in the temperature range of 20-50 K. Based on theoretical analysis, an expression for the admittance of an electrically active grain boundary at low temperatures was obtained. It was concluded that the relaxation of the shallow donors is Debye type with a thermally activated relaxation time and is related to the ionization process of these donors. The activation energy for the relaxation, i.e., the ionization energy of the shallow donors, was determined to be about 0.04 eV, the capture cross section of the shallow donors to be around 10(-12) cm(2), and the relaxation time at room temperature to be about 10(-13) s. (C) 2003 American Institute of Physics.

palavras-chave

ZINC-OXIDE VARISTORS; DEFECT CHEMISTRY; CERAMICS; TRANSPORT; BARRIERS; CO

categoria

Physics

autores

Han, JP; Senos, AMR; Mantas, PQ; Cao, WW

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".