Al-doped apatite-type nanocrystalline lanthanum silicates prepared by mechanochemical synthesis: Phase, structural and microstructural study

resumo

Al-doped La(9.33+x/3+y)Si(6-x)Al(x)O(26+3y/2) (x = 0-1.5, y = 0-0.67) apatite-type lanthanum silicates (ATLS) were synthesized with a high-power (1200 rpm) planetary ball mill that allows the formation of the lanthanum silicate phase after milling for 20-35 min at room temperature. The apatite phase already appears after milling for 5 min. Phase, structural and microstructural studies on the nanocrystalline lanthanum silicates were carried out by using XRD, TEM, and IR, (27)Al and (29)Si MAS NMR spectroscopy to clarify the mechanism of ATLS formation. The cluster-topotactic mechanism of the formation of apatite by mechanochemical treatment involving hydration of the starting compounds and acid-base reactions is suggested, Al-doping results in promoting the formation of apatite. However, a secondary LaAlO(3) phase may be present in the sample depending on its stoichiometry. This suggests the existence of a biphase domain in the La(2)O(3)-SiO(2)-Al(2)O(3) phase diagram at room temperature, in which Al-doped apatite and LaAlO(3) phases coexist. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2008).

palavras-chave

OXIDE FUEL-CELLS; SOL-GEL PROCESS; IONIC-CONDUCTIVITY; OXYAPATITE; ROUTE; GD; ND; SM; DY; LA9.33SI6O26

categoria

Chemistry

autores

Kharlamova, T; Pavlova, S; Sadykov, V; Chaikina, M; Krieger, T; Lapina, O; Khabibulin, D; Ishchenko, A; Zaikovskii, V; Argirusis, C; Frade, J

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".