Influence of external compressive stress on the ionic conductivity of melt-quenched lithium silicate (15Li(2)O-85SiO(2)) glass

resumo

This paper reports measurements of the electrical resistances of bulk and milled amorphous lithium silicate (15Li(2)O-85SiO(2)) under uniaxial load at 200 degrees C. With imposed load up to 700 MPa, the resistance of the melt quenched glass increases from 1.56 to 1.95 M Omega cm. This change is reversible, namely after releasing the load the initial electrical resistance is recovered. Milled and compacted glass consists of the bulk and particle contacts resistances. Both of them increase when the external compression up to 200 MPa. For the bulk element, when compression is released, the initial resistance is recovered, whereas the resistance changes within the particles contacts are irreversible. (C) 2016 Elsevier B.V. All rights reserved.

palavras-chave

MECHANOCHEMICAL SYNTHESIS; LI CONDUCTIVITY; SYSTEM; PRESSURE; CRYSTALLIZATION; LI2O-SIO2; BATTERIES

categoria

Chemistry; Physics

autores

Graczyk-Zajac, M; Vrankovic, D; Schader, FH; Fernandes, HR; Tulyaganov, DU

nossos autores

agradecimentos

We thank Prof. Norbert Nicoloso and Prof. Kyle G. Webber for fruitful discussions and manuscript proofreading. F.H.S. gratefully acknowledges financial support from the Deutsche Forschungsgemeinschaft under WE 4972/2. Authors thank Christina Stabler for the help in the sample preparation.

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".