Linear and nonlinear optical investigations of N:ZnO/ITO thin films system for opto-electronic functions


Different concentrations of N (0, 1, 3 and 5 wt.%) added ZnO thin films were primed using spin coater. X-ray diffraction (XRD) patterns confirm the preferred growth orientation of all films along (0 0 2) plane, however, ITO has dominant features owing to low thickness of the films. XRD along with vibrational spectroscopy confirms the single hexagonal phase of ZnO. The crystallite size evaluated from Scherrer's equation increased with increase in N-doping concentrations and is found to lie in the range of 25-36 nm. The increased crystallite size reduces the dislocation density which confirms the reduction of defects in the films. The dislocation density (delta) is found to be 1.569, 1.369, 0.984, and 0.965 for 0, 1, 3 and 5 wt.% N doped ZnO films. N doping in ZnO was confirmed by EDX analysis and its homogeneous distribution was further confirmed by SEM mapping. AFM study confirms the formation of spherical nanoparticles whose size increase with increase in N doping, validating the XRD results. The films are found to have similar to 80% transparency which is quite impressive from window layer application point of view. Absorption edge is found to be red shifted owing to N doping, indicating a reduction in energy gap. Hence energy gap was evaluated using Tauc's relation and is found to reduce from 3.43 to 3.14 eV (Delta E = 0.29 eV) with in content of N-doping. The absorption index, refractive index, real and imaginary dielectric constants were also estimated. The values of chi((1)) and chi((3)) are estimated to be in range of 0.3-9 and 1.0 x 10(-11) -1.0 x 10(-8) , respectively. The Nanocrystalline films with spherical nanocrystallites, high optical transparency and non-linear properties recommend their application in opto-electronic technology.




Optics; Physics


Arif, M; Shkir, M; AlFaify, S; Sanger, A; Vilarinho, PM; Singh, A

nossos autores


The authors are grateful to Department of Science and Technology Ministry of Science and Technology & University Grants Commission, Government of India for the financial support. A.S. would like to thank the Department of Science & Technology, Ministry of Science & Technology, Govt. of India for the award of Young Scientist and BOYCAST Fellowship. The authors M.S. and S.A. would like to express their gratitude to King Khalid University, Saudi Arabia for providing administrative and technical support. Authors are also thankful to Prof. I.S. Yahia, KKU, KSA for help in OC.

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".