Three-dimensional fcc C60 polymer


A face-centered cubic (fcc) polymerized C60 phase has been synthesized at 9.5 GPa and 550 ¡C. The observed short lattice constant, 13.19 , indicates that a three-dimensional (3D) polymer with adjacent C60 molecules covalently bonded was obtained. Possible polymerized structures, with each molecule adopting one of the two standard orientations, have been investigated through density functional theory (DFT). It was found that intermolecular bonds, 56/56 2 + 2 cycloaddition, are formed between molecules with different orientations but no bonds are formed between molecules with the same orientation. The computed bulk moduli for these structures gave values ranging from 88 to 132 GPa. Although the distances between neighboring molecules and the volume per molecule from the models are close to the experimental values, the relaxed structures displayed symmetries lower than cubic, suggesting that the experimental fcc structure is likely disordered or frustrated. © 2019


Laranjeira J.; Marques L.; Melle-Franco M.; Struty_ski K.; Mezouar M.; Barroso M.

nossos autores


This work was supported by the projects POCI-01-0145-FEDER-031326 financed by the Portuguese Foundation for Science and Technology (FCT) and co-financed by FEDER . CICECO-Aveiro Institute of Materials, FCT Ref. UID/CTM/50011/2019, financed by national funds through the FCT/MCTES and IF/00894/2015 finances by FCT. J. Laranjeira acknowledges a PhD grant from FCT (SFRH/BD/139327/2018).

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".