Transport properties and thermal expansion of perovskite-like La0.3Sr0.7Fe(Al,Cr)O3-delta ceramics

resumo

The use of perovskite-like (Sr,La)FeO3-delta as ceramic membrane materials requires extensive doping in order to increase stability and to suppress thermal and chemical induced expansion. The substitution of iron with aluminum and chromium in La0.3Sr0.7Fe1-x-yAlxCryO3-delta (x=0-0.4; y=0-0.2) was found to decrease total conductivity, oxygen permeability and thermal expansion coefficients. The oxygen ion transference. numbers of La0.3Sr0.7Fe(Al,Cr)O3-delta, determined by faradaic efficiency measurements in air, vary in the range 10(-4) to 10(-2) at 1073-1223 K, increasing with temperature. The incorporation of chromium into perovskite lattice enhances the low-p(O-2) stability down to oxygen partial pressures of 2 x 10(-15) to 2 x 10(-14) Pa at 1173-1223 K. The solid solution formation is, however, limited to the values of x approximate to 0.30-0.35 and y approximate to 0.07-0.08. (c) 2005 Elsevier Ltd. All rights reserved.

palavras-chave

OXYGEN-TRANSPORT; IONIC TRANSPORT; ELECTROLYTE; PERMEATION; MEMBRANES

categoria

Materials Science

autores

Yaremchenko, AA; Kharton, VV; Shaula, AL; Patrakeev, MV; Marques, FMB

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".