"Greening" the synthesis of SrBi229TaO thin films

resumo

A new procedure based on an ethanolic solution of the appropriate cations to obtain SrBi2Ta2O9 (SBT) thin films is described, reducing the necessity of toxic organicals. According to X-ray diffraction analysis the desired SBT crystalline phase is obtained after heat treatment at 720 degrees C, in air, for 20 min. The ferroelectric properties of the obtained thin film include a remnant polarization value of 5,0 mu C/cm(2) and a coercive field of 50 kV/cm, which are rather good results for a stoichiometric SBT thin film. (C) 2005 Elsevier B.V. All rights reserved.

palavras-chave

SRBI2NB2O9

categoria

Materials Science; Physics

autores

Gonzalez-Aguilar, G; Salvado, IMM; Costa, MEV

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".