Mixed conductivity and stability of CaFe2O4-delta

resumo

The total conductivity of CaFe2O4-delta, studied in the oxygen partial pressure range from 10(-17) to 0.5 atm at 1023-1223 K, is predominantly p-type electronic under oxidizing conditions. The oxygen ion transference numbers determined by the steady-state oxygen permeation and faradaic efficiency measurements vary in the range of 0.2 to 7.2 x 10(-4) at 1123-1273 K, increasing with temperature. No evidence of any significant cationic contribution to the conductivity was found. The Mossbauer spectroscopy, thermogravimetry, and X-ray diffraction (XRD) showed that the orthorhombic lattice of calcium ferrite is essentially intolerant to the oxygen vacancy formation and to doping with lower-valence cations, such as Co and Ni. The oxygen nonstoichiometry (delta) is almost negligible, 0.0046-0.0059 at 973-1223 K and p(O-2) = 10(-5)-0.21 atm, providing a substantial dimensional stability of CaFe2O4-delta ceramics. The average linear thermal expansion coefficients, calculated from the controlled-atmosphere dilatometry and high-temperature XRD data, are (9.6-13.9) x 10(-6) K-1 in the oxygen pressure range from 10(-8) to 0.21 atm at 873-1373 K. Decreasing P(02) results in a modest lattice contraction and in the p-n transition indicated by the conductivity and Seebeck coefficient variations. The phase decomposition of CaFe2O4-delta occurs at oxygen chemical potentials between the low-p(O-2) stability limit of Ca2Fe2O5-delta brownmillerite and the hematite/magnetite boundary in binary Fe-O system. (c) 2008 The Electrochemical Society.

palavras-chave

THERMAL-EXPANSION; ELECTRONIC TRANSPORT; IONIC-CONDUCTIVITY; PARTIAL OXIDATION; MEMBRANE REACTOR; OXYGEN; PEROVSKITES; OXIDES; CERAMICS; NONSTOICHIOMETRY

categoria

Electrochemistry; Materials Science

autores

Kharton, VV; Tsipis, EV; Kolotygin, VA; Avdeev, M; Viskup, AP; Waerenborgh, JC; Frade, JR

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".