resumo
Driven by a need to develop low-cost and thermally stable materials for thermoelectric applications, donor-substituted strontium titanate is considered as a promising alternative to traditional thermoelectrics. The complex defect chemistry of SrTiO3-based materials imposes various limitations on identifying the relevant effects exerted on the electronic band structure and heat transfer, being a subject of debate and intensive research. Based on combined XRD, SEM/EDS, HRTEM, XPS, and TGA studies and measurements of thermoelectric properties, this work uncovers the particular role of various structural defects in electrical and thermal transport in Sr1 +/- yTi0.9Nb0.1O3 +/-delta, selected as a model system. Introduction of A-site cation vacancies provides a synergistic effect of combining fast charge transport in the perovskite lattice and suppressing the thermal conductivity mostly due to simultaneous generation of oxygen vacancies. The presence of oxygen vacancies promotes more efficient phonon scattering compared to Ruddlesden-Popper-type layers. These findings provide a link between structural and thermoelectric properties, offering further prospects for seeking highly performing SrTiO3-based thermoelectrics by tailoring the defect chemistry mechanisms.
palavras-chave
NB-DOPED SRTIO3; ELECTRONIC TRANSPORT-PROPERTIES; THERMAL-CONDUCTIVITY; POWER-GENERATION; VACANCY CLUSTERS; SINGLE-CRYSTALS; THIN-FILMS; PERFORMANCE; CERAMICS; OXIDE
categoria
Chemistry; Energy & Fuels; Materials Science
autores
Kovalevsky, AV; Aguirre, MH; Populoh, S; Patricio, SG; Ferreira, NM; Mikhalev, SM; Fagg, DP; Weidenkaff, A; Frade, JR
nossos autores
Andrei Kavaleuski
Investigador principal
Jorge Ribeiro Frade
Professor(a) Jubilado(a)
Nuno Miguel Freitas Ferreira
Bolseiro de pós-Doutoramento
Sergey Mikhalev
Bolseiro de pós-Doutoramento
Sónia Gonçalves Patrício
Investigador AuxiliarGrupos
G3 - Materiais Eletroquímicos, Interfaces e Revestimentos
G5 - Materiais Biomiméticos, Biológicos e Vivos
agradecimentos
This work was supported by the FCT (grants IF/00302/2012, IF/01344/2014 and SFRH/BPD/75943/2011), and projects CICECO-Aveiro Institute of Materials (ref. UID/CTM/50011/2013), and PTDC/CTM-ENE/6319/2014, financed by COMPETE 2020 Programme and National Funds through the FCT/MEC and when applicable co-financed by FEDER under the PT2020 Partnership Agreement. The authors are thankful to Prof. Carlos Sa (CEMUP) for performing XPS studies and helpful discussion of the results, M. J. de Pinho Bastos (UA) for her assistance with XRD analysis and Dr P. Thiel (Empa) and J. Macias (UA) for their technical and experimental support. TEM studies were conducted at LMA-INA with financial support of Marie Curie-Career Integration Grant Project No. 304043.