Influence of processing route on microstructure and mechanical properties of MgAl2O4 spinel


This paper reports on process dependant microstructural and mechanical properties of MgAl2O4 spinel (MAS) ceramics. Two MAS powders with different chemical compositions were synthesized by solid-state reaction of alumina and calcined caustic magnesia at 1400 degrees C for I It. The surface of the as obtained MAS powders was passivated against hydrolysis by coating it with H3PO4 and Al(H2PO4)(3) species dissolved in ethanol at 80 degrees C for 24 It. The as protected powders could then be dispersed in aqueous solutions of tetramethylammonium hydroxide (TMAH) and Duramax D-3005 as dispersing agents to obtain stable slurries with 45 vol.% solids loading. The stable aqueous MAS slurries were consolidated by slip casting (SC), gelcasting (GC), hydrolysis assisted solidification (HAS) and hydrolysis induced aqueous gelcasting (GCHAS) routes, fully dried and then sintered for I h at 1650 degrees C. For comparison purposes, dense MAS ceramics were also prepared following a conventional dry-powder pressing (DP) and temperature induced gelation (TIG) routes. All the sintered MAS ceramics were thoroughly characterized for bulk density, apparent porosity, water absorption capacity, SEM microstructure, XRD phase, hardness, 3-point bend strength, and percentage of shrinkage to evaluate the suitability of the processing routes for fabricating defect free components with near-net shape. Among the various techniques employed, the GCHAS was found to be best for fabricating near-net shape MAS ceramics. (C) 2009 Elsevier Ltd and Techna Group S.r.l. All rights reserved.




Materials Science


Ganesh, I; Reddy, GJ; Sundararajan, G; Olhero, SM; Torres, PMC; Ferreira, JMF

nossos autores


IG thanks SERC-DST (Government of India) for the awarded BOYSCAST fellowship (SR/BY/E-04/06). S.M. Olhero wishes to thank to Foundation for Science and Technology (FCT) of Portugal for the financial support under the grant SFRH/BPD/27013/2006. The financial support of CICECO is also acknowledged. GJR thanks Director, ARCI for awarding senior ARCI fellowship (SAF). Authors wish to thank the distinguished reviewer for his valuable and constructive comments that have improved the quality of the paper.

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".