Multiferroic properties of BiFeO3 doped Bi(MgTi)O-3-PbTiO3 ceramic system

resumo

Ceramic samples of [BiFeO3](y)(BiMg0.5Ti0.5O3)(1-y)](0.55)[PbTiO3](0.45) designated as (BF-BMT-PT) were prepared by high temperature solid-state reaction method. X-ray diffraction analysis of the powder samples suggests the formation of a single-phase material with transformation from rhombohedral to tetragonal crystal structure with increase in BF content. Polarization vs electric field (P-E) hysteresis studies show maximum remanent polarization (P-r similar to 1.4 mu C/cm(2)) for composition y = 0.08. Dielectric studies of the compounds as a function of temperature at frequency 100 kHz show that the compounds undergo a diffuse phase transition with a transition temperature increasing with increasing y. The diffusivity parameter of the phase transition for these compounds yielded values between 1.6 and 1.8 indicating significant variation of degree of disordering in the system. (C) 2010 Elsevier B.V. All rights reserved.

palavras-chave

MORPHOTROPIC PHASE-BOUNDARY; HIGH-TEMPERATURE; SOLID-SOLUTION; ELECTRIC POLARIZATION; DIELECTRIC-PROPERTIES; PIEZOELECTRIC SYSTEM; MAGNETIC-PROPERTIES; PT CERAMICS; THIN-FILM; PIEZOCERAMICS

categoria

Chemistry; Materials Science; Metallurgy & Metallurgical Engineering

autores

Rai, R; Kholkin, AL; Sharma, S

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".