Influence of pH on the corrosion protection of epoxy-silica-zirconia sol-gel coatings applied on EN AW-6063 aluminium alloy

abstract

Aluminium alloys of 6000 series can suffer severe corrosion in polluted (acidic) and/or marine environments and in contact with alkaline media like fresh cementitious materials. Therefore, architectural aluminium components are often coated, what requires its surface pre-treatment. Organic-inorganic hybrid (OIH) sol-gel coatings have been proposed as an effective, environmental compliant new pre-treatment for aluminium coating. In this work, an epoxy-silica-zirconia sol-gel coating was synthesized and applied on EN AW-6063 alloy. Cerium nitrate was incorporated as corrosion inhibitor. Cerium doped and undoped OIH coatings were exposed to neutral, acidic (pH similar to 3) and alkaline (pH similar to 10) chloride solutions. Electrochemical impedance spectroscopy (EIS) and SEM/EDS characterization of coated samples revealed that the best performance is achieved in the neutral and the worst in the acidic solution. In the alkaline solution, the cerium doped coatings exhibited much better anticorrosive performance than the undoped ones, clearly evidencing the beneficial role of the corrosion inhibitor in this media.

keywords

PERFORMANCE; INHIBITION

subject category

Electrochemistry

authors

Fontinha, IR; Salta, MM; Zheludkevich, ML; Ferreira, MGS; Figueira, RB; Pereira, EV; Silva, CJR

our authors

Share this project:

Related Publications

We use cookies for marketing activities and to offer you a better experience. By clicking “Accept Cookies” you agree with our cookie policy. Read about how we use cookies by clicking "Privacy and Cookie Policy".