Mild hydrothermal synthesis, crystal structure, photoluminescence properties and emission quantum yield of a new zirconium germanate with garnet-type structure

abstract

The mild hydrothermal synthesis, crystal structure, photoluminescence properties and emission quantum yield of a new sodium zirconium germanate are reported. This material and the method for its preparation represent for the first time a germanium garnet-type material synthesized at autogenous pressure and temperature at 230 degrees C. The crystal structure was determined by starting from the crystallographic parameters of a common garnet structure and it represents not only a new chemical combination of atoms but also combination of oxidation states in garnet structure. The framework consists of interconnected corner sharing GeO4 tetrahedra and ZrO6 octahedra which form small cavities that accommodate charge compensation Na+ cations. In the course of synthesis the structure can be functionalized by in situ doping with different percentage of Eu3+ ions. This structural flexibility is used to explore the photoluminescent behavior of the active centers embedded in garnet-type host. The materials display the Eu3+ (D0 -> F0-4)-D-5-F-7 transitions under excitation via intra-(4)f(6) excitation levels and through the O2- -> Eu3+ ligand-to-metal charge transfer. A maximum D-5(0) quantum efficiency and emission quantum yield values (ca. 0.28 and 0.04 +/- 0.01, respectively) were found for the low Eu3+-containing sample, suggesting the presence of concentration quenching effects at higher Eu3+-content (5%). (C) 2012 Elsevier Inc. All rights reserved.

keywords

SINGLE-CRYSTALS; LUMINESCENCE; IONS; DIFFRACTION; TB3AL5O12; SPECTRA; CE3+

subject category

Chemistry

authors

Ferdov, S; Ferreira, RAS; Lin, Z; Wu, ZY

our authors

acknowledgements

This work was supported by FCT, project PTDC/CTM/108953/2008.

Share this project:

Related Publications

We use cookies for marketing activities and to offer you a better experience. By clicking “Accept Cookies” you agree with our cookie policy. Read about how we use cookies by clicking "Privacy and Cookie Policy".