High-pressure zinc oxysulphide phases in the ZnO-ZnS system

resumo

Wurtzite-zincblende mixture, ZnO-ZnS (1:1wt.%), was thermally treated at 5GPa in order to explore a possible mutual solubility of the end members and formation of zinc oxysulphide phases under high pressure. The data on phase content, crystal structure, and microstructure from the X-ray diffraction and the scanning electron microscopy studies of the obtained compacts (ceramics) were compared and analyzed. It was found that as temperature is increased, the following processes occur in the ZnO-ZnS mixture under pressure: release of the mechanical stresses (between about 300 and 700 degrees C), recrystallization of the initial wurtzite and zincblende phases (700-900 degrees C), reaction between the end members (above approximate to 900 degrees C) that results in formation of mixed oxysulphides based on ZnO and ZnS, respectively, with the mutual solubility rate of about 8mol.%.

palavras-chave

FILMS; DIFFRACTION; PARAMETERS; DEPOSITION; RICH

categoria

Materials Science; Physics

autores

Salak, AN; Ignatenko, OV; Zhaludkevich, AL; Lisenkov, AD; Starykevich, M; Zheludkevich, ML; Ferreira, MGS

nossos autores

agradecimentos

This work was supported by the MSCA project

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".