resumo
This study seeks the valorization of industrial residues (fly ash and construction and demolition waste (CDW)) through the production of geopolymer mortars. The effect of the sand substitution by CDW and the influence of the particle size range of CDW fine aggregates on the fresh and hardened properties of the mortars were evaluated. Geopolymer mortars were produced using biomass fly ash waste and metakaolin as a binder, CDW as fine aggregates, and an alkali solution of sodium silicate and sodium hydroxide as activator. The geopolymer mortars were characterized in fresh state by the flow table test and in the hardened state through chemical, physical/microstructural analyzes. The mortars produced with CDW showed lower flowability when compared to the ones prepared with sand. The compressive and flexural strength of hardened mortars, respectively, obtained with residues were higher when compared to sand: 40 MPa and 8.5 MPa with CDW, against 23 MPa and 3.1 MPa for sand-based samples. It was observed that mortars developed with recycled aggregate and natural aggregate present similar chemical and mineralogical compositions. The superior results obtained in the mechanical properties of mortars produced with CDW are related to the recycled aggregate-geopolymer paste interface. (C) 2019 Institution of Chemical Engineers. Published by Elsevier B.V. All rights reserved.
palavras-chave
CONCRETE; CEMENT; PERFORMANCE; AGGREGATE; STRENGTH
categoria
Engineering
autores
De Rossi, A; Ribeiro, MJ; Labrincha, JA; Novais, RM; Hotza, D; Moreira, RFPM
nossos autores
João António Labrincha Baptista
Professor Catedrático
Rui Miguel Novais
Professor Auxiliaragradecimentos
This work was developed in the scope of the project CAPES/FCT 88887.125458/2016-00. The funding agencies CAPES and CNPq (Brazil) and FCT (Portugal) are thus gratefully acknowledged.